The metal would overheat and even burn under the thermal shock arisen as laser drilling,which causes micro damage inside the metal.Void damage is the most important origin for crack propagation and failure of metal.To understand the damage mechanism in the heat affected zone of the high temperature nickel based superalloy DD6,a microvoid nucleation experiment was designed and implemented by laser drilling in DD6 sheet.The complex characteristics of micro-damage including micro-voids near the perforation were observed by scanning electron microscopy.An analytic solution of the temperature field in DD6 sheet for thermal shock arisen as laser drilling was obtained on the basis of the non-Fourier heat conduction theory.As a result,the minimum of peak temperature during the thermal shock in the zone of microvoid nucleation was estimated.