【摘 要】
：
In order to improve the visible light photocatalytic activity of TiO2,many approaches like coupled with other oxides,doping with nonmetal elements have been developed.However,to the best of our knowle
【机 构】
：
The Xinjiang Technical Institute of Physics & Chemisty;Key Laboratory of Functional Materials and De
【出 处】
：
第十四届全国太阳能光化学与光催化学术会议
论文部分内容阅读
In order to improve the visible light photocatalytic activity of TiO2,many approaches like coupled with other oxides,doping with nonmetal elements have been developed.However,to the best of our knowledge,limited work has been done on the mesoporous carbon and titania nano/heterojunction with graphene carbon nitride(g-C3N4)for the purpose of solar conversion.Herein,we present the fabrication and characterization of mesoporous g-C3N4/C-TiO2 ternary nanojunction.Such architecture provides a broadening optical window for effective light harvesting,short diffusion distance for excellent charge transport,as well as a large contact area for fast interfacial charge separation and photoelectrochemical reactions.As a result,this material is anticipated to exhibit good photocatalytic activity,as eviced by the degradation of methylenblue(MB)under visible light.
其他文献
硫化氢(H2S)是石油、天然气加工过程中伴生的有害气体，具有毒性高、产量大等特点。虽然H2S通常被认为是一种负担，但其组分H2和S却具有巨大的经济价值 [1]。工业主要采用Claus工艺对H2S进行处理，通过氧气作用实现H2S的部分氧化得到硫磺和水，其缺点之一是H2S中的H2没能得到有效利用 [2]。为解决该问题，人们提出的一种方案是利用太阳能采光(电)催化的方法对H2S进行处理 [3]。但现有的
采用共沉淀-水热方法,以金属钽粉为原料,合成了具有中空结构的Na2Ta2O6纳米空心球.研究了矿化剂、反应时间、反应温度对样品形貌、尺寸、晶化程度和光催化产氢活性的影响规律.结果表明矿化剂的浓度对样品的形貌、尺寸、净化程度和光催化产氢活性的影响较大.当NaF浓度较小时,样品呈球状,且大小不均匀,延长反应时间导致空心球粒径变大.增大NaF的浓度后,样品呈明显空心球结构,形貌规整,空心球具有较大的比表
Direct water splitting on a semiconductor photocatalyst is one of the simplest and the most important reaction in artificial photosynthesis.For practical application,development of highly active visib
量子点敏化太阳能电池(QDSSC)的光阳极结构是影响电荷传输复合的重要因素之一[1,2],我们以TiO2 微球结构和P25 纳米晶为基础制备了两种量子点敏化太阳能电池Cell-SP 与Cell-P25.Cell-SP 的光电转化效率可达到4.2％,明显高于P25 量子点电池效率(3.8％).两种电池具有类似的填充因子和开路电压,其光电性能的差异主要源于Cell-SP 较高的短路光电流.通常认为,微
石墨烯,一种二维、单层碳原子蜂窝状结构的新型材料,利用其比表面积大、电子传导能力强等特点改善TiO2的光催化性能逐渐成为当前的热点之一[1].本文以石墨粉为原料,通过改进的Hummer氧化法[2]制备氧化石墨,对其超声分离得到澄清的氧化石墨烯溶液(Graphene Oxide,GO).以P25为原料在强碱介质中通过水热法制备TiO2纳米线(Nanowair,NW).将两者混合,通过水热合成法制备了
无牺牲试剂下完全分解水制氢对控制制氢成本具有重要意义,是未来大规模制氢的必然选择[1].与牺牲试剂下产氢不同,完全分解水过程中产氧往往成为反应过程的控制步骤[2].本文利用光化学沉积法负载Pt,Rh 物种于光催化材料HKLBT.光催化活性测试(表1)显示Rh 负载后HKLBT 具有完全分解水的能力(H2/O2≈2),而负载Pt 后虽然明显提高了产氢量,但并未增加O2 的比例((H2/O2＞3),氢
Photocatalysis is a promising water purification method due to its potential of using solar energy directly and achieving both microbial disinfection and chemical detoxification.There are some propose
染料敏化太阳能电池作为第三代光伏电池，具有效率高、组装简便、成本低廉等诸多优势，在过去二十年间受到了广泛的关注[1]。其最高效率已经达到了13％[2]。染料敏化太阳能电池一般由三个部分组成：由染料敏化的半导体薄膜所组成的光阳极、含有氧化还原对的电解液和具有催化活性的贵金属对电极。当染料受光激发，所产生的光生电子会迅速传导到半导体薄膜的导带，随后通过在半导体薄膜内部的传输到达集流体，再通过外电路及其
Hollow and mesoporous hierarchical microstructures have been found to be an attractive class of materials for their superior physical properties and potential applications.Different structures of ZnTe
半导体量子点理论上在一个高能量光子作用下，能产生多个激子(电子-空穴对)，即多重激子效应，利用其制备的激子型太阳能电池，如量子点敏化太阳能电池，可以突破传统P-N 结太阳能电池的Shockley-Queisser 极限(33％)模型，期望获得更高的光电转换效率(41％)。目前以CdS/CdSe 共敏化太阳能电池的效率最好，其电池结构如图1 所示。但是与传统太阳能电池相比，其光电转换效率依然较低(～