M(o)ssbauer Spectroscopic Study on Ancient Goryeo Celadon

• 作 者: Woo-Seok CHO Hyunggoo NO Ungsoo KIM Jong-Young KIM Chin Mo KIM Chul Sung KIM Gyung In
• 机 构: Korea Institute of Ceramic Engineering and Technology,Icheon-si,Gyeonggi-do 467-843,Republic of Kore
• 出 处: 2015中国(景德镇)高技术陶瓷国际论坛暨第九届亚洲陶瓷材料研讨会
• 发表日期: 2015年9期
• 关键词: raw Materials m(o)ssbauer spectroscopy celadon chromaticity colorative mechanism

　　In ancient Goryeo celadon excavated from the kiln sites in GangJin and Buan areas, the effect of the chemical composition and ionic state of Fe on the color was evaluated by M(o)ssbauer spectroscopy and chromaticity analysis.According to chromaticity analysis, the L* value (brightness) of the glaze was shown to be affected more by TiO2 and MnO than by Fe2O3, and the body was affected more by Fe2O3 than by TiO2.The a* value was found to be affected by Fe2O3 and TiO2 in the glaze, whereas there was nearly no change in the body according to the composition.As for the b* value, changes due to the composition was shown to be smaller than those for the L* and a* values.According to M(o)ssbauer spectroscopy results, as the quantity of TiO2 and Fe2O3 is increased, Fe2+/Fe3+ decreases; while the change of Fe2+/Fe3+ upon MnO and P2O5 is negligible.As the quantity of Fe2+/Fe3+ increases, the a* and b* values decrease, which results in the change of color from red-yellow to blue-green.The characteristic green color can be attributed to increased L* (brightness) and decreased a*/b* values (blue-green shift) due to the reduced Fe ion, which is mainly determined by the TiO2 and Fe2O3.