【摘 要】
：
In this paper,cuprous oxide nanosheets/graphene oxide composites (Cu2O-GO) are prepared using a simple solution approach and subsequent annealing at 400 ℃.The morphology and structure of as-prepared C
【机 构】
：
State Key Laboratory of Chemical Resource Engineering,Key Laboratory of Carbon Fiber and Functional
论文部分内容阅读
In this paper,cuprous oxide nanosheets/graphene oxide composites (Cu2O-GO) are prepared using a simple solution approach and subsequent annealing at 400 ℃.The morphology and structure of as-prepared Cu2O/GO are characterized by scanning electron microscopy (SEM),transmission electron microscopy (TEM) and X-ray diffraction (XRD).It is found that the Cu2O nanosheets with the average size of ca.200 nm and average thickness of ca.20 nm are layed homogeneously and anchored closely on the graphene oxide (GO) surface.The composite,used as the anode materials,exhibits excellent electrochemical performance.The reversible capacity is up to ca.447.5 mAhg-1 at 50mAg-1,and the corresponding coulombic efficiency is about 60%.At the higher current densities of 500 and lOOOmAg-1,the reversible capacity can reach 346.5 and 301.2mAhg-1 respectively.The excellent elec-trochemical performance should be attributed to the 2D laminated structure of Cu20 as well as close connection between graphene and Cu2O: (1) 2D laminated structure of Cu2O can withstand more impact from the insertion/desertion of lithium-ion compared with other structures such as nanoparticles.(2) Both the 2D structures and close connection make the conductive network of GO and Cu2O more stable.Therefore,the Cu2O-GO shows the great potential for application in the anode.
其他文献
等离子体发射光谱是探究等离子体参数、等离子体基团分布的有效工具.本文利用发射光谱技术对CH4/H2微波等离子体进行原位在线测量,研究了沉积过程中等离子体内部的基团种类以及气压对等离子体中各基团谱线强度的影响,测量分析了等离子体中各基团的空间分布以及气压对空间分布的影响.结果表明,随着气压的升高,Hα、CH、C2基团的发射光谱强度先增大后减小,且发射光谱线强度都在30kPa附近达到最大值.发射光强度
本文以短切酚醛纤维或硫酸钙晶须为增强组元,采用液相加压发泡/炭化工艺制得纳米孔径结构的酚醛树脂基泡沫炭.采用扫描电子显微镜,压汞仪,万能材料试验机,热扩散系数分析仪和差示扫描量热仪对泡沫炭材料的微观形貌,孔结构,机械性能及热性能进行分析和表征,研究了不同增强组元对树脂基泡沫炭的结构及性能的影响.结果表明:与纯酚醛树脂基泡沫炭相比,添加增强组元后制备的泡沫炭微观形貌变化不大,孔径呈单峰集中分布,孔径
微波等离子体化学气相沉积法是一种理想的生长单晶金刚石的方法.本文以压缩波导结构微波等离子体源谐振腔为腔体,高温高压(HPHT)金刚石单晶片为衬底,在较高工作气压下进行了单晶金刚石的同质外延生长.利用扫描电子显微镜(SEM)和激光Raman光谱仪分别对金刚石的表面形貌和质量进行了表征.发现甲烷浓度对同质外延生长出的金刚石的形貌和速率有显著的影响,高的甲烷度能得到高的生长速率,但形貌不理想;而较低的甲
鉴于质子辐照拥有可以造成较高厚度均匀损伤区的优势,本实验采用3MeV质子辐照核石墨IG-110,获得一个80ym厚度左右的均匀损伤区来模拟研究中子辐照所造成的损伤情况.辐照前后石墨表面微结构变化以及力学性能(硬度、模量)变化,分别使用扫描电子显微镜和纳米压痕仪来表征.结果显示石墨表面片状微晶尺寸变小呈皲裂碎屑状,而力学强度增强为初始的两倍.辐照引起石墨内部缺陷的演化情况采用场发射透射电子显微镜以及
Porous SnO2/carbon microsphere composite has been prepared by a simple hydrothermal method combined with a sub-sequent ZnC12 activation.The composite mainly in spherical shape with particle size rangi
以聚苯并嗯嗪为前躯体,合成了具有大孔容的珊瑚状含氮中孔炭.材料具有可连续调控的孔容积,最大孔容可达5.16 cm3g-1.这种珊瑚状炭材料是由囊泡状基本单元所构成的具有开放性孔道的连续骨架,并且在囊泡的一侧都具有开口,开口尺寸约为22 nm,基本单元之间有一定的连续性和连通性,,并且材料的比表面积主要是由2nm中孔贡献,这将有利于电解质离子接触材料表面,提高材料表面的利用率,使其可以作为更好的超级
超级电容器以其高功率密度、稳定的循环性能以及环境友好等优点成为了新一代的电化学储能装置.活性碳纤维由于拥有较高的比表面积、微小的孔径以及较好的电子导电性而成为了超级电容器理想的电极材料.本文以聚丙烯晴基预氧丝为原料采用CO2活化法制备了活性碳纤维,以6mol/L的KOH溶液作为电解液采用双电极方法对材料进行了循环伏安和恒流充放电测试,测得其比电容可以达到120 F/g.即使在100 mA/cm2的
以石墨烯/氧化锰复合材料为正极、以活性碳纤维为负极在Imol.L-1 Na2SO4溶液中组装出新型非对称超级电容器.采用循环伏安、恒流充放电、交流阻抗等电化学方法对其电化学性能进行测试.结果表明,优化后的非对称超级电容器可在1.8V的电压区间内进行可逆充放电,最大能量密度可达51.1Wh.kg-1.另外,该非对称超级电容器显示出良好的循环稳定性,经过1000次循环后容量保持率为97％.
首次以80.3％Co3O4@19.7％ rGO复合材料为正极,AC为负极,6M KOH溶液为电解液组装成80.3％ Co3O4@ 19.7％ rGO/AC非对称超级电容器并测试其电化学性能;测试结果显示,基于80.3％Co3O4@ 19.7％rGO复合材料电极的电容器电位窗口从0.5V扩展到1.5V,容量达114.1 F·g-1,且表现出良好的电容特性和大电流放电性能.电化学性能的改善得益于以较大
采用商业超级电容器用活性炭作为活性材料,在不同的测试温度下,运用循环伏安、恒流充放电、交流阻抗等表征方法研究了新型电解质四氟硼酸螺旋双吡咯烷鎓(SBP-BF4)与四氟硼酸四乙基铵(Et4 NBF4)在碳酸丙烯酯(PC)中的电化学性能差异.结果表明,SBP-BF4在常温(25℃)、高温(60℃)以及低温(-20℃)条件下的电化学性能均优于Et4NBF4.在-20℃环境下,SBP-BF4电解液中,0.