【摘 要】
：
The 0.30 mm grain-oriented silicon steel was scribed by laser equipment.The effect of parameters such as laser power, laser frequency, scanning speed and scribing spacing on the domain width were inve
【机 构】
：
School of Energy Power and Mechanical Engineering, North China Electric Power University, Beijing 10
【出 处】
：
第十四届中国体视学与图像分析学术会议
论文部分内容阅读
The 0.30 mm grain-oriented silicon steel was scribed by laser equipment.The effect of parameters such as laser power, laser frequency, scanning speed and scribing spacing on the domain width were investigated.The micro-topography of nicks under different parameters were observed.The optimized parameters of laser scribing makes domain width reduce to 0.355 mm.The depth of nicks increases when the laser power increases and decreases when the scanning speed increases.The laser frequency has little effect on the depth of nicks.
其他文献
为了实现机载激光雷达数据的有效应用,需要对激光雷达数据的进行分类.本文提出了一种新的只利用激光雷达高程数据将研究区域分为屋顶、树、地面和其他四类对象的方法.区别于其他方法,此方法分两步实现,首先利用监督分类方法将研究区域分为屋顶、树和其他;为了达到高的精度,该步骤在特征和分类器选择上都针对分类目标和特点进行定制.第二步利用滤波方法将非屋顶和非树的对象分类地面与其他对象.实验结果表明,本文提出的方法
本文提出了一种在压缩域中实现红外小目标检测的新方法.该方法首先将原始红外小目标图像分离成背景图像和目标图像,再对目标图像进行压缩得到目标压缩量测,然后利用目标图像压缩量测实现红外小目标检测.对比传统的基于压缩感知(CS)的红外小目标检测方法,该方法不仅能够在不恢复任何原始信号的前提下,对不同背景的红外小目标图像进行目标检测,且具有检测速度更快、占用内存以及计算量更小等优点.实验结果表明该方法能够实
二维谱估计算法Capon以及Apes在合成孔径雷达(SAR)超分辨成像中得到了较广泛的应用,但这两种算法无法同时满足高分辨率和高精度幅度估计的要求.前人已经提出了将两者相结合的一维Capes算法,本文在此基础上,提出和实现了二维Capes算法,通过对SAR实测数据的成像处理,验证了算法的有效性.结果表明,应用二维Capes算法所得到的SAR图像,同时具有较好的超分辨率和准确的幅度估计.
图匹配问题是计算机视觉中一个重要而基础的问题.针对图匹配问题目前最优的求解方法是凸-凹松弛过程(CCRP).但是,CCRP方法需要对一系列松弛问题进行求解,使得其速度较慢,难以求解大规模图匹配问题.同时图匹配中的约束条件与马尔科夫随机场最大后验概率推理中的约束条件具有相似性.受此启发,作者将图匹配问题表示为一个特殊的约束下马尔科夫随机场最大后验概率推理问题.在此基础上,针对该问题,作者提出一种新型
CT(computed tomography)为计算机断层成像,是现代医学重要的影像学检查诊断技术之一.三维口腔锥束CT能够得到与实际结构一致的三维高分辨率解剖图像,有助于医生定性定量的分析口腔部位的形态结构、病变组织等.本文基于口腔CT图像,研究了全景图自动合成与牙根管中心轴自动提取两个方面的内容:(1)本文首先根据牙弓线,得到连续的牙齿矢状面剖切图,然后在连续牙齿矢状面剖切图上提取全景图拟合曲
The significant distribution of {411 } texture exists during the preparation of thin-gauge grain-oriented silicon steels, which has effect on the abnormal growth of Goss grains during the secondary r
The duplex stainless steels after solid solution at different temperature were subjected to the same cold rolling and annealing for varied time at 1323 K.The interfacial boundary character distributio
为获取足够多数量的真实晶粒样本,对纯铁晶粒组织进行了大尺度的三维重建.重建实验方法采用系列截面法,分析范围为1.3mm×1.8mm×0.54mm,实验获取了二维系列截面300张.针对大尺度情况下三维重建工作量急剧增加等问题,对晶界提取与封闭、晶粒分割等图像处理过程进行了优化.采用计算机与人工相结合的方法在保证重建精度的情况下大大提高了重建效率,在可接受的时间范围内完成了大尺度纯铁晶粒组织的三维重建
2205双相不锈钢在一定温度下时效处理会产生析出相,冷轧变形处理会影响析出相析出,进而影响其耐蚀性能.文本研究了热轧与冷轧2205双相不锈钢析出相与腐蚀规律的联系.利用光学显微镜(OM)和扫描电子显微镜(SEM)配合能谱仪(EDS)观察了析出相显微组织的变化,利用X射线衍射仪(XRD)对冷轧变形过程中可能出现的应变诱发马氏体及析出相进行分析.结果表明,在850℃时效会依次析出x相和σ相,经冷轧变形
利用相变法可在低牌号电工钢中制备出强{100}织构晶粒,从而有效地提高磁性能.将5mm厚的实验钢热轧板冷轧至0.2mm厚,然后分别在不同的热处理工艺下进行相变退火.利用电子背散射衍射(EBSD)技术获得热处理后样品的取向数据图.结果表明,在4L/minH2较低流量下,较低温度(1000℃)退火后的板材中形成了两个半厚的柱状晶组织,主要为{110}织构;而在8L/minH2较高流量下,较低温度退火后