【摘 要】
：
In this paper, the electrically conductive PI nanofibrous composites with a certain anmout of multi-walled carbon nanotubes (MWCNTs) werepapared by electrospinning technique.In order to realize unitor
【机 构】
：
Lab of Dielectric Polymer Materials and Devices, University of Science and Technology Beijing, Beiji
论文部分内容阅读
In this paper, the electrically conductive PI nanofibrous composites with a certain anmout of multi-walled carbon nanotubes (MWCNTs) werepapared by electrospinning technique.In order to realize unitorm MWCNTs dispersion in the PI nanofibers,the functional groups was introduced on the surface of MWCNTs by chemical functiongalization.And the poly(ethylene oxide) (PEO) was used as a dispersing medium and it was finally removed by imidization process. The surface morphlolgy of the electrospum nanofibrous composites were observed by scanning electron microscope (SEM,JSM-7500F Hitachi,Japan) as shown in Figure 1a-d.The MWCNTs dispersion in the PEO nanofibers was investigated by transmission electron microscope (TEM,H-7650B Hitachi,Japan) as shown in Figure 1e-f.
其他文献
利用电声脉冲(PEA)方法测试了在不同热压温度、不同热压压力下制备的低密度聚乙烯/低密度聚乙烯(LDPE/LDPE)双夹层试样的空间电荷分布情况.分析了夹层热压温度和压力对该绝缘体界面处空间电荷特性的影响.结果表明,随着夹层热压温度的升高,物理界面变小,总空间电荷量先减小后增加.夹层热压压力对LDPE/LDPE界面的空间电荷分布影响较小.
本文通过热脉冲法和光刺激放电法研究了聚酰亚胺薄膜中陷阱能级分布情形.利用热脉冲法监测样品中的空间电荷分布变化,发现样品中的电荷衰减速率随短路时间的增加而减小,通过计算电荷量随时间的变化得到了聚酰亚胺的两个陷阱能级.同时采用光刺激放电法测量到在250 nm到600 nm光波段内,聚酰亚胺也存在有两个陷阱能级(分别位于413 nm和290 nm附近),这两个陷阱能级较由监测等温电荷衰减所得到的两个陷阱
BSCT/PVDF composites were prepared by solution casting with DMF as solvent. The addition of BSCT had significant influence on the crystallization, melting, and glass transition behaviors of the PVDF m
SF6在PD作用下的分解特性不仅与绝缘故障类型及故障程度有关,而且还与设备中H2O的含量关系密切.这就会造成SF6即使是在相同强度PD作用下的分解特性也会因气室内H2O含量的不同而不同,这就为利用SF6在PD作用下的分解特性来评判SF6电气设备绝缘故障带来了极大的困难.因此,获取H2O含量对SF6分解特性的影响规律及其校正方法,是本领域需要解决的基础问题之一.然而,目前关于这方面的研究还未见相关卓
气体组分分析故障诊断法的可靠性或有效性取决于对PD导致SF6分解组分检测的准确性,由于对微量O2的检测精度有限,目前几乎所有研究含O2体积分数都比较高,远远超过了IEC60376-2004所允许的运行状态下SF6设备O2含量值≤0.6％的最高水平和国家电力行业标准DL/T941-2005所允许的O2含量值≤0.2％的最高水平,对于运行状态允许范围内的痕量O2对SF6分解特性和用于SF6设备故障诊断
MAGNETICALLY insulated inductive voltage adders (MIVA) are widely used in applications of X-rays radiography and effect simulations. At present in almost all MIVA cells, the transformer oil is chosen
空间电荷对高压电力电缆材料的老化和击穿过程中有着十分重要的影响,而空间电荷包现象与电介质绝缘材料的击穿特性有密切关系.通过研究低密度聚乙烯(LDPE)中的空间电荷包的迁移行为,可以得到空间电荷包的宏观迁移率.通过电子束辐照将电荷注入至样品近表面处,并利用压力波法(pressure wave propagation,PWP)监测在外加电场的推动下原辐照注入的电荷所形成的空间电荷包在样品中的迁移情况.
本文研究了直接氟化对环氧绝缘表面电学性能的影响.研究结果显示在室温至95℃的范围内改变氟化温度会导致环氧绝缘的表面电导率变化(增加)近4个数量级.而氟化时间的延长会引起表面电导率一定程度的减小.表面电位测量表明存在一个临界表面电导率,在这个临界值以上初始表面电位随表面电导率的增加快速地减小、以致到零.红外分析和扫描电子显微镜观察揭示氟化导致了环氧表层物化特征的本质变化.这些变化密切关联于氟化温度和
文章研究添加剂对低密度聚乙烯(LDPE)空间电荷的影响,主要采用分子模拟技术,将经过能量优化后的纳米颗粒添加到LDPE,运用分子动力学原理与密度泛函数相结合分析纳米复合材料的空间电荷分布,并对其分布规律进行相关分析.通过对LDPE与纳米复合材料电荷密度的比较,结果表明:纳米粒子对LDPE空间电荷具有良好的抑制效果,同时对其抑制机理进行了相关分析.
随着高压直流输电的发展,直流电缆的应用日益广泛,交联聚乙烯及其复合材料受到广泛关注和研究.目前针对250kV及以上电压等级的高压直流电缆的试验标准并不完善,尤其是直流老化寿命指数的选取,直接决定了预鉴定试验和型式试验的电压,但由于传统的加速寿命试验难以快速准确的获得直流下的老化寿命指数,因此只能借鉴交流下的值作为参考.而研究表明电缆绝缘在直流和交流下的老化机理不同,直流下的老化受空间电荷积聚的影响