For the purpose of obtaining the optimal microstructures and mechanical properties of the CGHAZ under high input welding,continuous cooling transformation diagrams of the coarse grain heat-affected zo
【机 构】
：
State Key Laboratory of Metastable Materials Science and Technology Yanshan University Qinhuangdao,0
论文部分内容阅读
For the purpose of obtaining the optimal microstructures and mechanical properties of the CGHAZ under high input welding,continuous cooling transformation diagrams of the coarse grain heat-affected zone(CGHAZ)and the corresponding microstructures were investigated for a E36 class V-N-Ti,V-Ti,and Nb-Ti shipbuilding steels.The results indicated that the CGHAZ continuous transformation behaviors of Nb-Ti and V-Ti steel were similar,but the V-retard phenomenon was not as apparent as that of Nb.In addition,the cooling rate of ferrite transformation of V-Ti steel was higher than that of Nb-Ti steel.The nitrogen addition in the V-Ti steel enhanced the ferrite transformation,since that increasing the nitrogen could obtain fine(Ti,V)(C,N)particles and refine the original austenite size,which can promote the ferrite nucleation.The bainite transformation range of V-N-Ti steel was obviously lower than that of Nb-Ti,V-Ti steel at the t8/5≥100s.
其他文献
Before being subjected to water quenched,16mm WDL690D steel was heated at 910℃,930℃,950℃and 970℃for 20min,40min and 60min,respectively.Microstructures of these samples after heat treatment were observ
A new V-Ti-Mo complex micro-alloyed hot-rolled high strength sheet steel was developed by controlling a thermomechanical controlled processing(TMCP)schedule,in particular with variants in coiling temp
To develop thickness>60mm,yield strength>550MPa high-strength steel plate,the effects of heat treatment process on the microstructure and mechanical properties of plate specimens were investigated on
Potential benefits of vanadium in heat treated medium carbon bar steels are considered by reviewing examples from several recent studies.Emphasis is placed on microstructural development,strength,and
An new method is proposed to predict in sequence the phase transformation behavior and the depth of the decarburized ferrite layer with simultaneous scaling of a steel during cooling process from the
We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering.Detailed isothermal treatments were made a
690MPa high strength steel with low yield ratio for building structure has been developed successfully by micro-alloying design and thermal-mechanical controlled processing in WISCO.The mechanical pro
In the shipbuilding industry,the welding efficiency of the ship plate not only has a great effect on the construction cost of the ship,but also affects the construction speed and determines the delive
In multi-pass welding process,various thermal cycle of both weld metal(WM)and heat affected zone(HAZ)will be subjected several times.This will make the initial microstructure occur an irreversible tra
Effect of heat-affected zone(HAZ)on spot weldability in automotive hot stamping(HS)steel sheet was investigated for automotive applications.Tensile test was performed on a tensile testing machine at a