重稀土Lu掺杂增强Sm2Co17永磁体的矫顽力机理研究

来源 :第十六届全国磁学和磁性材料会议暨第十七届全国微波磁学会议 | 被引量 : 0次 | 上传用户：chen95127

【摘要】

：

稀土NdFeB永磁材料的发展开创了高性能永磁材料的新篇章,但在高温应用领域,其矫顽力随温度升高的衰减很快.目前人们主要通过添加重稀土元素(如Dy、Te 等)来提高磁体的矫顽力,但最终仍然无法解决NdFeB 磁体的矫顽力温度系数高的问题.S m2Co17 烧结永磁体自问世以来,凭其具有高的居里温度(820℃)和强抗氧化性,特别是高矫顽力等性能,得到广泛的应用,在国防工业、尖端技术、航空航天等领域具有

【作者】

：

张朋越卢阳春丁丽菁马正怀吴琼王秀敏葛洪良

【机构】

：

中国计量学院浙江省磁学重点实验室,浙江杭州310018 浙江凯文磁业有限公司,浙江东阳 32210

【出处】

：

第十六届全国磁学和磁性材料会议暨第十七届全国微波磁学会议

【发表日期】

：

2015年11期

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

The silicon dioxide barrier films influence on the laser ablation destruction of the glass composite

The oxide films drawing from the solutions-sols is simple performed and therefore the rather demanded method.One of the most vital issues is the uncontrollable components diffusion from the substrate

会议

Formation of metallic sodium nanoparticles in fluorine phosphate and silicate glasses by thermal tre

Two methods of formation of metallic sodium nanoparticles in bulk of fluorine phosphate glass and on surface of silicate glasses glass by thermal treatment and electron beam processing have been demon

会议

Influence of environment on the photodestruction of silver nanoparticles in photo-thermo-refractive

Phototermorefractive (PTR) glasses are perspective material for recording of highly efficient volume phase holograms operating in red visible and near IR spectral range (700-3000 nm).

会议

Laser-Welding of Transparent Materials Using Luminescent Glass Sealants

Laser welding of transparent materials mediated by a laser light-absorbing interlayer is a promising technique, not only for its process speed, but also for the highly localized bonding area, which mi

会议

The Immobilisation of Irradiated Graphite in Calcium Aluminosilicate Glass Composite Materials Using

Identifying a long-term immobilisation and disposal ronte for ～260 000 tonnes of irradiated graphite remains a major challenge.Previously, we studied the use of microwave processing technique to produ

会议

The study of soda-lime silicate flat glass strengthening by spraying

At present, the immersing technology is a mainly method for the soda-lime silicate flat glass strengthening,which are immerged into molten salt at a certain temperature for some hours.

会议

How advanced are the Advanced Process Control technologies for glass melting furnaces

Since the eighties of the 20th century supervisory control systems have been used in the glass industry.Model Predictive Control (MPC) technology, which was developed in the chemical industry, was int

会议

The influence of different oxidising agents on the iron redox reaction in silicate melts using in-si

The redox state of iron in glasses depends on temperature, oxygen fugacity and chemical composition and influences the properties of silicate glasses l.The thermodynamics of redox reactions involving

会议

Sm(CobalFexCu0.08Zr0.06)7.4合金磁特性和显微结构研究

在Sm2Co17烧结永磁体中,Fe原子主要进入Sm2(Co,Fe)17 主相中,通过部分取代Co 原子提高磁体的内禀饱和磁化强度和剩余磁化强度.Livingston的研究提出Fe 元素有助于磁体内部胞状组织的形成,胞状组织以Sm2(Co,Fe)17 作为主相,Sm(Co,Cu)5 作为胞壁相[1].因此,Fe 元素在2:17 型SmCo 烧结永磁体中的含量和分布对其微结构和磁性能有着密切联系.因此

会议

MnBi1-xTix合金的微结构与磁性能的影响

近年来,随着世界稀土资源的日益减少,急需开发新型高磁性无稀土永磁体.无稀土永磁MnBi合金具有价格低廉、不易腐蚀、力学性能好等优点,同时又具有较高永磁特性,特别是它在一定温度范围内矫顽力呈正的温度系数,这对开发高温工作电机具有重要的意义.

会议

重稀土Lu掺杂增强Sm2Co17永磁体的矫顽力机理研究

其他学术论文