RESEARCH ON MICROSTRUCTURES AND MECHANICAL PROP ERTIES OF FIBER LASER WELDING OF A7N01 AL-ALLOY

来源 :第四届微试样测试技术国际学术会议((The 4th International Conference on Small | 被引量 : 0次 | 上传用户：lhcllk

【摘要】

：

A7N01 aluminum alloy with the thickness of 10mm is welded using fiber las er with filler wire,the microstructures and mechanical properties of the weld ing joints are observed and analyzed by microhar

【作者】

：

JIANG Yi-shuai YANG Shang-lei WANG Yan YANG Zhi-hua

【机构】

：

School of Materials Engineering,Shanghai University of Engineering Scienc e,Shanghai 201620,China

【出处】

：

第四届微试样测试技术国际学术会议((The 4th International Conference on Small

【发表日期】

：

2016年4期

【关键词】

：

Aluminum alloy laser welding Microstructure mechanical Prop erty

下载到本地 , 更方便阅读

下载此文赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

其他文献

STRAIN CORRECTION IN SMALL SPECIMEN TENSILE TEST WITHOUT EXTENSOMETER

Small specimen is widely used in mechanical test of reactor structural materials due to the limited volume in irradiation facility and less activity after irradiated.

会议

AN ALTERNATIVE METHOD FOR STRAIN-CONTROLLED FATIGUE TEST AT ELEVATED TEMPERATURE

For strain-controlled fatigue tests,especially at elevated temperature,implementation of knife-edges and punching dimples within gauge length of specimen may cause premature failure on the test sectio

会议

EVALUATION OF CREEP DEFORMATION BY INDENTATION TEST WITH A CONSTANT DEPTH-APPLICABILITY FOR INHOMOGE

Toevaluate the strength reliability of the electronic substrate,it is requiredto obtain the creep properties of the solder joint in-situ.The indentation test is one of effective method to evaluate the

会议

DETERMINATION OF CREEP DAMAGE PROPERTIES FROM A MINIATURE THREE POINT BENDING SPECIMEN USING AN INVE

In this work,a novel method for determining the creep damage properties which can be used to represent the full life until failure from a miniature bending creep test specimen is developed based on a

会议

Creep damage propertiesminiature specimenthree-point bendinginverse approach

IMPROVEMENT OF PREDICTING MECHANICAL PROPERTIES FROM SPHERICAL INDENTATION TEST

Although nowadays the Instrumented Indentation Test(IIT)can be applied to the fields from nano-micro-to macroscopic scale,this paper only addresses its application in the area of life assessment of co

会议

STUDY OF FATIGUE PROPERTIES OF MATERIALS THROUGH BALL INDENTATION AND SMALL PUNCH TEST METHODS

Fatigue property of materials is an important input while estimating the residual life of critical components,as,fatigue data(stress vs.cycles or strain vs.cycles or fatigue crack growth rate data)are

会议

VERIFICATION AND CALIBRATION OF INSTRUMENTED INDENTATION TESTING MACHINES

The frame compliance is calibrated by experimental and calculation methods for an instrumented equipment.The indentation depth and diameter with single cycle test is determined by confocal laser scann

会议

CORRELATION FACTOR STUDY OF SMALL PUNCH CREEP TEST AND ITS LIFE PREDICTION

Small punch test is one of the innovative methods that can be used to evaluate the properties of material without destructive harm to the in-service component.

会议

Small Punch Creep TestUniaxial Creep TestCorrelation FactorLife Prediction

SURFACE DEFECT INSPECTION OF PRESSURE EQUIPMENT BASED ON INDENTATION AND NUMERICAL SIMULATION

Surface defects caused by damage or corrosion are major factor in petrochemical pressure vessels and line pipes failure.The characteristic size of typical surface defect is from micron to submillimete

会议

Surface defectIndentationStochastic characteristics

MECHANICAL BEHAVIOR EVALUATION OF A ARC WELDED NICKEL-ALUMINUM BRONZE ALLOY WITH MICRO INDENTATION M

In this research,the mechanical behavior of a multi-pass gas tungsten arc welded nickel–aluminum bronze(NAB)alloy is investigated.Macro-tensile testing shows the mechanical behavior difference of the

会议

mechanical behaviortensile testmicro indentationnickel-aluminum bronz

RESEARCH ON MICROSTRUCTURES AND MECHANICAL PROP ERTIES OF FIBER LASER WELDING OF A7N01 AL-ALLOY

其他学术论文