【摘 要】
：
The slag non-autoclaved and unburned brick(SNAUB) was prepared on laboratory scale using the high titania BF slag (HTBFS) as aggregate, styrene-acrylate emulsion as cementing materials and two admixtu
【机 构】
：
Dongbci University of Materials and Metallurgy,Shenyang,Liaoning;Shenyang Institute of Chemical Tech
【出 处】
：
2004年有色金属冶金及材料第二届国际学术会议
论文部分内容阅读
The slag non-autoclaved and unburned brick(SNAUB) was prepared on laboratory scale using the high titania BF slag (HTBFS) as aggregate, styrene-acrylate emulsion as cementing materials and two admixtures. Factors such as amounts of admixtures and styrene-acrylate emulsion, forming pressure and curing system on product properties were studied. The optional conditions for preparing the SNAUB were obtained as following : admixture 1 8％-10％, admixture 2 8％-9％, styrene-acrylate emulsion 8％-10％, forming pressure 30MPa, curing time 7d. The properties of the SNAUB are better than that of MU 25.
其他文献
镁合金化学镀层的孔隙率与其耐蚀性有着直接的关系.根据基体元素与相应的指示剂显色原理,采用贴试纸法,对镁合金化学镀层的孔隙率测定进行了研究,并考察了镀液参数对孔隙率的影响.通过电子扫描电镜(SEM)和镀层的耐蚀性测试,验证贴试纸法测镁合金化学镀层孔隙率可行性.结果表明,铬黑T作指示剂溶液测定镁合金化学镀层孔隙率效果最佳,镁试剂I效果次之,茜素磺酸钠指示剂最差;采用贴试纸法测定化学镀层孔隙率是可行的;
A clear zinc hydrometallurgical process-the hydrometallurgy of zinc without iron residue was proposed in this paper. By using iron and part of zinc in the zinc sulfidc concentrates and manganese in py
Nickel-sulfur electrode was obtained in a modified Watts bath by adding thiourea (TU) into the bath. The effects of TU concentration, current density, temperature and pH value of electrodepositing sol
A new type of metal matrix composite with a composition of Al2O3-33.8Fe-26.2Ni (wt.％) used as inert anode was developed in this article. Aluminum electrolysis with this anode was conducted for 12 hour
The power feeding curve of graphitized furnace is a key technique in production of the electrode. The furnace is improved in order to reduce the power consumption of the electrode, to cut short the po
In the blast furnace slag, titanium disseminates in various mineral phases(perovskite, spinel, Ti-rich diopside, Ti(C、 N) and titannaugite). Based on the technique of selective precipitation, titanium
According to the thermogravimetric analysis of cobalt oxalate, different micropowder of Co3O4 was prepared from cobalt oxalate by thermal decomposition at different condition, which was characterized
A series of the electrode materials (LiCoO2) for Lithium ion batteries were synthesized by radiating the mixture of Lithium oxide and Cobalt oxide in microwave field. The synthesizing conditions inclu
As well known, there exists a reciprocal relationshipbetween refractories industry and high temperatureindustries, in particular metallurgy industry.Refractories are consumed in many metallurgicalproc
Ni-S-Co alloy was prepared by electrodeposition in a modified Watts bath with addition of thiourea (TU) and CoCl2. The structure and morphology were determined by XRD and SEM respectively. The content