本文采用电化学法对La(Fe,Si)13系材料进行渗氢,通过实验研究电解温度对渗氢过程的影响。采用XRD和SEM对物相及表面形貌进行分析,并利用VSM检测样品的磁性能。实验结果表明：电解温度的提升有助于电化学渗氢反应的进行；
La(Fe,Si)13系材料电化学渗氢及其致冷性能
【摘 要】
：
本文采用电化学法对La(Fe,Si)13系材料进行渗氢,通过实验研究电解温度对渗氢过程的影响。采用XRD和SEM对物相及表面形貌进行分析,并利用VSM检测样品的磁性能。实验结果表明：电解温度的提升有助于电化学渗氢反应的进行；
【机 构】
：
材料科学与工程学院,西安理工大学,西安710048
【出 处】
：
2014中国功能材料科技与产业高层论坛
【发表日期】
：
2014年2期
其他文献
In order to short reduction period, decrease energy consumption and lower labour-intensive in the production of Mg reduction, a kind of vertical and fast reduction Mg furnace was developed to come int
Mesoporous ZnO thin film is an important part of dye-sensitized solar cells (DSSCs) due to it determines the amount of adsorbed dyes.However, small specific surface area of ZnO thin film prepared by o
Facile synthesis of CaCO3 and CaCO3∶Eu3+ phosphors by solid state reaction at room temperature and t
The CaCO3 and CaCO3∶Eu3+ phosphors have been synthesized by solid state reaction at room temperature without further sintering treatment.
水热条件下，以双氧水和钼粉制备的过氧钼酸溶胶为钼源，乙醇为还原剂制备得到二氧化钼纳米棒。利用X-射线衍射(XRD)、扫描电子显微镜(SEM)以及场发射高分辨透射电子显微镜(HRTEM)对产物的结构与形貌进行表征。
Influence of fabrication parameter on the nanostructure of SiNWs under HF/AgNO3/Fe (NO3)3 etching sy
Large-area SiNWs has been successfully fabricated through one-step metal-assisted chemical etching process at room temperature.The effects of key fabrication parameters (AgNO3 concentration, Fe (NO3)3
This article describes the results of an experient of the photochemistry of the Omnicat 650 and 550 photoinitiators and an evaluation of their efficiency in the photopolymerizations of several differe
Chemical Structure Changes and Correlation Analysis of High Density Polyethylene after Natural and X
Elucidation of the chemical structure changes that take place of high density polyethylene (HDPE) used as rotational packaging case by attenuated total reflection infrared spectroscopy (ATR-FTIR),when
实验以铝粉和硅酸钠为主要原料，溶胶凝胶法制备球形SiO2-Al2O3复合除氟剂。采用XRD分析法对样品进行测试和表征，研究了SiO2含量、焙烧温度、焙烧时间和溶液pH值对除氟效果的影响。
Contact angle data for sets of probe liquids allow the determination of components of solid surface energies which in turn can be used to calculate the work of adhesion of oil to the solid surface.
Nano-TiO2 modified fluorine-containing polyacrylate soap-free emulsion was successfully synthesized via soap-free emulsion polymerization technique, in which the polymerization monomers consisted of M