【摘 要】
：
An in situ CeB6/Al inoculant was fabricated by arc melting technique and treated by melt-spinning at different cooling rates to improve its grain refining efficiency on pure aluminum.It has been found
【机 构】
：
Key Lab.for New Type of Functional Materials in Hebei Province,School of Materials Science and Engin
【出 处】
：
特种粉末冶金及复合材料制备/加工第一届学术会议
论文部分内容阅读
An in situ CeB6/Al inoculant was fabricated by arc melting technique and treated by melt-spinning at different cooling rates to improve its grain refining efficiency on pure aluminum.It has been found that the refractory CeB6 phase can be synthetic in Al melt and the size of CeB6 particles can be significantly reduced by applying different rotating speed of copper roller during melt-spinning.As a result, the CeB6 particles in ribbons has been reduced to ~500 nm at a high cooling rates of about 1.97x 107 K/s.The grain size of pure aluminum after inoculation can be refined to about 100 μm.The improved grain refinement of the in situ CeB6/Al inoculant can be attributed to the combining effect of nano-sized refiner particles and the excellent crystallography matching of CeB6 and Al.
其他文献
采用激光选区熔化工艺(SLM)分别沿垂直和水平方向成形Ti-15Nb(at.％)合金,研究其微观组织和力学性能各向异性.采用单轴拉伸试验测试了抗拉强度和断裂延伸率,利用SEM分析组织及断口形貌.结果表明,SLM成形Ti-15Nb合金的组织由针状马氏体和亚稳态B相组成,β相在垂直试样横截面上为细小胞状晶,在水平试样横截面上为拉长柱状晶,组织呈现出明显的各向异性.此外,其力学性能也表现出各向异性,沿垂
本文探讨了硬质合金内冷双螺旋孔棒材的制备技术,分析了此类棒材的国内生产现状.通过模具设计、国产挤压成型剂的开发、挤压工艺试验,研究了制备高速高效钻削用双螺旋孔棒材系列关键技术.实现了最小直径达Φ3.3mm等系列双螺旋孔棒材批量生产,产品螺旋角偏差小于±0.5°,达到国外著名K公司的公差要求,标志着我国制备螺旋孔棒的技术达到国际先进水平.
以Zr/Si混合粉体为浸渗原料,采用包埋法在C/C复合材料表面成功制备了SiC-ZrSi2复合涂层,用SEM和XRD表征了涂层的组成和结构,测试了涂层改性后C/C复合材料的力学性能及等离子体烧蚀性能.结果表明,涂层的主体相由SiC和ZrSi2相组成,还残留少量Si,涂层在C/C复合材料表面致密连续,厚度约为100μm,内部无穿透性裂纹;涂层改性后C/C复合材料的弯曲强度为192.38±6.84MP
空心球是一种新型壳层结构材料,其具有密度低、比表面积大、稳定性好等特性,近年来得到越来越多的关注.而SiC空心球凭借其独特的物理结构和优异的化学性能,在轻质填料、催化、保温隔热、复合材料等领域有着广阔的应用前景,SiC空心球的制备与应用成为研究人员的研究热点.本文综述了SiC空心球的几种常用制备方法,包括模板法、干凝胶法、溶剂热合成法,总结了近年来SiC空心球的应用进展,并对SiC空心球的进一步研
采用熔体反应法制备出新型的Al-Ti-B-C-Y中间合金孕育剂,对制备出的中间合金孕育剂铸锭进行真空快淬处理.经真空快淬处理后第二相颗粒更加细小(达到几十甚至十几纳米)分布更加均匀,有效增加了有效异质形核核心数量,提高了对焊接用铝铜合金基体的变质细化效果.分析研究C和稀土Y在中间合金孕育剂中的作用.用X射线衍射仪(XRD)分析其相组成,用扫描电镜(SEM)观察颗粒的分布及形貌.对用新型孕育剂变质细
对碳纳米管采用HNO3和H2SO4(体积分数1∶3)混酸纯化,并利用卧式高能球磨法制备了不同球磨时间和质量分数的碳纳米管与铝粉的复合粉末,用冷压-烧结工艺制备了CNTs/Al2024复合材料.对纯化后的碳纳米管进行XPS分析,使用扫描电子显微镜、透射电镜对复合材料的形貌进行表征;并测试了复合材料的抗拉强度、硬度.结果表明,混酸纯化除去了碳纳米管表面的杂质并引入了大量的含氧基团.当球磨时间为2.5h
The oxidation of Co-10Cr-xSi (x=0, 5, 10, nominal composition, at.%) alloys in 0.1Mpa pure O2 at 1073K was investigated.Co-10Cr presents the worst oxidation resistance with the mass gain of about 7.53
本文以Cr-Fe作为铜基粉末冶金摩擦材料中的摩擦组元,通过金相显微镜和电镜观察其微观组织,在摩擦磨损试验机MM3000上进行摩擦磨损实验,与含SiO2的铜基粉末冶金摩擦材料进行对比.结果表明:以Cr-Fe作为摩擦组元的铜基粉末冶金摩擦材料,结构上Cr-Fe与铜基体结合较为紧密,几乎没有可见的空隙.Cr-Fe含量12％(质量分数,下同)时摩擦系数最稳定,摩擦系数几乎不受摩擦速度的影响,并且磨损量也相
C/SiC复合材料在航空航天飞行器中应用的比重日益增大,并逐渐应用于前缘、控制翼等大型复杂结构,因此,C/SiC复合材料连接技术也逐渐成为C/SiC复合材料应用的研究重点.C/SiC复合材料销钉铆接技术具有连接强度可靠、热匹配良好,几乎不增加重量等优点,是C/SiC大型复杂结构最重要的连接技术之一.本文测试的C/SiC复合材料销钉采用化学气相渗透工艺(CVI)制造,销钉尺寸分别为Φ3和Φ4.5.由
采用自主研发的激光选区熔化(SLM)设备成形H13热作模具钢零件,研究了激光能量密度对材料性能的影响.研究结果表明:材料的相对致密度与激光能量密度成正比;硬度可达到国外同等材料锻件淬火后的硬度;常温拉伸强度可达到国外同等模具材料的性能,而塑性低于国家标准要求.