【摘 要】
：
In this talk scalable synthesis and characterization of holey graphene will be reported.Holey graphene is special graphene with great deal of through-thickn
【机 构】
：
CenterofNanomaterialsforRenewableEnergyStateKeyLaboratoryofElectricalInsulationandPowerEquipmentScho
【出 处】
：
2016石墨烯产业·技术高峰论坛暨第14届海峡两岸碳材料研讨会
论文部分内容阅读
In this talk scalable synthesis and characterization of holey graphene will be reported.Holey graphene is special graphene with great deal of through-thickness nano-holes distributed in its basal plain.Compared with regular graphene electrodes,the holes enable ions,e.g.Li+,H+,to transport faster and more efficiency in holey graphene electrodes so that holey graphene is greatly attractive in application of Li-ion batteries and supercapacitor currently.
其他文献
With the commercial application of graphite anode,lithium-ion batteries (LIBs) are extensively applied in numerous portable devices such as smartphones and
低维碳基纳米材料由于其独特的结构与性能引起学术界的广泛关注。特别是一维碳基纳米材料作为电极材料在储能器件中的应用引起了人们的高度重视。在本报告中，富碳化学与静
热管理领域中，炭基材料具有理论上的最高导热系数，而且其形态多样化化，可以是块体、薄膜、纤维、泡沫，粉体材料，也可以和其他材料复合满足热管理领域的应用需求；同时，树脂基泡沫
生物质柳絮具有天然高中空度的特殊中空管状结构,富含氮氧等杂原子,而且来源非常广泛,基于绿色环保、可持续的观点,柳絮是制备多孔炭材料的理想前驱体[1,2]。本文对生物
石墨烯(graphene)是碳原子以sp2键结形成蜂窝状排列且单原子层之二维结构的新型材料[1]，由于石墨烯具有优异的导电特性及极高的表面积[2-3]，当石墨烯与半导体材料复合时，可
中国推动石墨烯产业化如火如荼在各地展开，但几年过去了还是一筹莫展，让人不禁怀疑中国制造2025及十三五把石墨烯放进去政策是否是明智之举？其实，石墨烯做为「工业味精」的角
在C/C复合材料的CVI制备工艺中，如何缩短制备周期、制备微观结构可控的热解炭以及实现大尺寸样件的均匀沉积是该工艺主要的三大难点。结合C/C复合材料工业生产实际，利用气
化学还原氧化石墨烯(CRGO)不仅部分保留有石墨烯的电子共轭结构及其独特性能,同时其表面还残留一定数目的含氧官能团。这样与石墨烯相比较,CRGO更容易加工利用,这也预示
异质原子置换掺杂是调控石墨烯化学和电学性质的重要手段，目前较多的研究集中在氮掺杂石墨烯(NG)上，有关大面积硅掺杂石墨烯(SiG)和硼掺杂石墨烯(BG)的报道还很少。同时，对