【摘 要】
：
The recycled gypsum sample with sodium polyphosphate (STPP) was prepared under the condition of laboratory simulation.Then the sample was calcined to hemihydrate and carried out the tests of its mecha
【机 构】
：
College of Material Science and Engineering, Chongqing University, Chongqing 400045,China
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
The recycled gypsum sample with sodium polyphosphate (STPP) was prepared under the condition of laboratory simulation.Then the sample was calcined to hemihydrate and carried out the tests of its mechanical properties.By using modem testing instrument, such as SEM, Zeta potential analyzer, the effect of STPP on the performances of recycled gypsum and its change mechanism were analyzed.The results showed that the setting time and water-plaster weight ratio for standard consistency (W/P) of plaster of paris (POSP) with STPP were increased, which impaired the strength, while on the contrary, the setting time and W/P, strength of its recycled plaster (R-SP) were reduced and increased, respectively, compared with the recycled plaster (R-P) without STPP.And the strength was decreased to R-P and increased to R-SP, respectively, compared with POP and POSP.The analysis indicates STPP is selectively chemisorbed on the (111) face of gypsum crystal, it inhibits the growth in c axis direction, resulting in the transformation of morphology, thus making the hardened POSP crystals coarsened.When calcined, R-SP has rode-like crystals of low length-radius, also,-PO3Ca existing in the surface of R-SP increases the repulsive force between R-SP particles and improves their dispersion, which makes the W/P low, leading to the complete development of crystals and their close overlapping, thus reinforcing its hardened gypsum.
其他文献
The cement industry is aware of environmental problems due to large CO2 emission.Using less Portland cement can reduce the carbon footprint of the building industry.This can be achieved by using blend
Geopolymers belong to a new class of materials with features similar to ceramics.Compared to ceramics, the production process of geopolymers is however more energy efficient since it requires consolid
Geopolymerization is a complicated process.Even in a simple system consisting of an alkaline activator, such as water glass, and a silicate-aluminate material, such as fly ash, setting time and mechan
To reduce the negative influence of organic substance and P2O5 on crystal lattice, phosphogypsum was calcined into anhydrite at high temperature.The properties of anhydrite which were influenced by pr
Alkali-activated aluminosilicates (geopolymers) have been considered applicable substituent to ordinary Portland cement due to high performance and preferentially to reduced consumption of CaO, conseq
The production of highly reactive low temperature belite binder is one promising concept to reduce the energy demand and CO2 emissions in cement production.Belite has several well-known advantages in
This study assesses the impact of variations of the raw mix design, with respect to the type and proportions of calcium sulphate, and the effect of the clinkering process on mineral formation in calci
The present study aimed primarily to determine the effect of particle size distribution and the chemical and mineralogical composition of different types of Chinese fly ash on the nature of the reacti
Calcium sulfoaluminate cements (CSA) are a potential low CO2 alternative to Ordinary Portland cement.To further reduce the CO2 emissions related to CSA, they can be blended with supplementary cementit
One of the promising opportunities for a more environmentally friendly cement manufacture is the production of a clinker based on calcium sulfoaluminate (CSA).Although CSA clinkers may have quite vari