【摘 要】
：
In this study, three modeling experiments were designed to investigate whether nano-particles incorporated in the cement paste act as nucleation sites for C-S-H gel growth during cement hydration.The
【机 构】
：
College of Civil Engineering & Architecture, Zhejiang University of Technology,Hangzhou 310014, Chin
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
In this study, three modeling experiments were designed to investigate whether nano-particles incorporated in the cement paste act as nucleation sites for C-S-H gel growth during cement hydration.The nano-particles with (nano-SiO2) and without (nano-TiO2) pozzolanic reactivity were used as nano-particles.In the first experiment,both the cement and nano particles were dispersed in water to prepare dilute cement paste, in which the cement and nano-particles can contact each other.In the second one, the cement particles were laid inside a filter paper funnel and immersed in water with nano-particles dispersed, in order to separate the cement particles with nano-particles by using the filter paper.In the third one, large clinker particle was embedded in resin,surface-polished and then exposed upside down in water with nano-particles dispersed.After hydration for a certain curing age, the hydration products in the paste or the nano-paticle dispersion were observed by using TEM and the hydrated surface of the embedded clinkers were detected by using SEM.The results revealed that no C-S-H gel from cement hydration grew from nano-particles, implying that the nano-particles in the cement hydrating system cannot act as nucleation sites for C-S-H gel growth during cement hydration.
其他文献
Cement-asphalt mortar (CA mortar) is composed of Portland cement, asphalt emulsion,water and other admixtures,which combines both advantages of the mechanical property of cement and flexibility of asp
Although the C3A content in clinker is relatively low, its behavior is crucial because it controls the setting time of cement.The presence of minor elements, mainly alkalis (including Na+ and K+) duri
In this paper, the hydration process of Portland cement with NaCl and KCl addition was studied by isothermal calorimeter, ultrasonic method and compressive strength.Pastes were designed containing 5%,
In this study, synthetic C-S-H samples were investigated to reveal the feature at atomic scale.Rietveld refinement was applied to high resolution X-ray scattering data, yielding the lattice constants
In this paper, the capacity of solidification and mechanism of ettringite to heavy metal ions (Cr, Pb, Zn, Cd,Cu) with different valence and existence form were analyzed, and the curing stability of e
In recent years, a novel concept to accelerate cement hydration has been proposed by adding external nuclei into a hydrating cementitious system, which is called seeding technology.In this way, promot
Portland cement paste and Portland cement paste blended with fly ash aged 365 days were studied using synchrotron X-ray tomography with the pixel resolution of 0.74 μm at the BL13W1 beamline of the Sh
This paper presents a study on the effect of fine ferric hydroxide and gypsum on the properties of oil-well cement slurry and hardened oil-well cement slurry in the temperature condition of 750C.Since
The microstructures of Portland cement paste (water to cement ratio is 0.4, curing time is from 1 day to 28 days) are simulated based on the numerical cement hydration model, HUMOSTRUC3D (van Breugel,
The self-healing of cement-based materials incorporating mineral additives in groundwater condition was studied.More work was done to investigate the process of the crystallization of calcium carbonat