【摘 要】
：
The aim of the test is to research the influence rules of TEA·HCl on the workability of cement paste and concrete.Based on the features of the new hardening accelerator, we established experimental an
【机 构】
：
The School of Materials Science and Engineering, Shenyang Jianzhu University, Shenyang 110168, China
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
The aim of the test is to research the influence rules of TEA·HCl on the workability of cement paste and concrete.Based on the features of the new hardening accelerator, we established experimental analysis system through different dosages of hardening accelerator, and verified the feasibility of such accelerator to satisfy the need of practical engineering.The results show that adding of the hardening accelerator can accelerate the cement hydration, and what is more,when the dosage was 0.04%, the setting time was the shortest while the initial setting time and final setting time were 130min and 180min, respectively.The initial fluidity of cement paste of adding accelerator was roughly equivalent compared with that of blank.After 30min, fluidity loss would be decreased with the dosage increasing, but fluidity may be increased.The application of the hardening accelerator can make the early workability of concrete to be improved, especially the slump loss of 30min can be improved more significantly.The bleeding rate of concrete was significantly decreased after adding TEA·HC1.The conclusion is that the new hardening accelerator can meet the need of the workability of cement-based materials in the optimum dosage range.
其他文献
崇越电通创立于1981年，代理销售台湾端以及日本信越化学工业株式会社之Silicone产品.近年因应市场端Touch Panel客户需求，针对metal mesh制程引进一系列相关之配套材料供客户使用.其中，尤以软模压印方式制作Metal Mesh制程中所需的材料为关键因素之一.崇越电通提供软模压印所合适之材料，并将于论坛中说明材料特性，并分析其应用性.1.PDMS离模剂2.压印胶3.底涂4.奈米
Solidification/stabilization of municipal solid waste incineration (MSWI) fly ash, especially from fluidized bed incinerators, with Portland cement and water is difficult, because it causes the evolut
The influence of heat curing was considered which it has on the hydration and silicate structure of cement paste (CP) and silica fume paste (SFP).The influences were discussed from the perspectives of
In the present paper a new accelerating additive for cement mixtures, based on transition metal silicate hydrates,is described.The new additive is highly effective in promoting the nucleation and grow
Superplasticizers and retarders are essential in the production of many cementitious materials.While superplasticizers enhance the cement paste flowability, retarders allows for the tuning of the sett
Polycarboxylate ether type superplasticizer (PCE) is widely used nowadays in concrete industry due to its high dispersion ability and versatility.The number and type of carboxylic groups, the number a
Temperature changes driven by hydration reactions and environmental loading cause thermal cracking of restrained concrete elements.This work describes the use of microencapsulated phase change materia
The retarding grinding aid(DE) which synthesized by Diethanolamine(DEA), Epichlorohydrin and sodium hydroxide was characterized by infra-red spectroscopy(FT-IR) and used for the production of Portland
The variation of initial fluidity and fluidity retention of cement pastes were tested to evaluate the compatibility between polycarboxylate superplasticizer (PC) and cements which was produced by addi
C-S-H seeding is a relativley new approach to accelerate cement hydration.C-S-H nanoparticles are added to the cement lime to stimulate the formation of C-S-H nuclei during very early stage of cement