【摘 要】
：
The influence of residual stress on stress corrosion behavior was studied by way of SSRT test on the base metal of X80 pipe with different residual tensile stress in the simulating soil environment aq
【机 构】
：
Tubular Goods Research Institute of CNPC Key Laboratory of Petroleum Tubular Goods Engineering of CN
【出 处】
：
2015年油气输送管道高强度管线钢研究与应用技术国际研习会
论文部分内容阅读
The influence of residual stress on stress corrosion behavior was studied by way of SSRT test on the base metal of X80 pipe with different residual tensile stress in the simulating soil environment aqueous solution; and the electrochemical test techniques were adopted to test the effect of the residual stress on electrochemical polarization behavior and AC impedance characteristics of the base metal.It is shown that the base metal specimens without introducing the residual stress of X80 UOE pipe and X80 SAWH pipe have different stress corrosion sensitivity in this solution.The base metal specimens with different residual stress of X80 pipe only occurs the anodic metal dissolution reaction on the material surface in this kind of solution without forming the passive film.The residual tensile stress leads to the increase of the electrochemical activity and the reduction of impedance of the base metal surface of X80 pipe,and it accelerates the nucleation and early propagation of the stress corrosion crack,which promotes the SCC sensitivity of the base metal.
其他文献
在全球能源匮乏和自然资源备受关注的背景下,大多数国家对工业废弃物在工程应用中具有的经济、环保和技术方面的优势表现出极大的兴趣,许多工业废弃物被证明在减少水泥生产时对环境污染方面有很大的贡献.具有低碳、节能、环保等诸多优势.水泥、混凝土行业有着优良的生态形象,建材行业是工业废弃物消耗量最大、最直接的,也是最能充分利用的行业之一. 固体废弃物的危害表现在侵占土地、污染土壤、污染水体等方面。我国冶金行业
本文采用淬火变形膨胀仪DIL805A,经10℃/s加热至920℃后保温10min,再分别以0.5-100℃/s不同的冷却速度冷却到室温,获得X90管线钢CCT曲线.同时采用光学显微分析仪对不同冷却速度下的X90试样进行了微观组织分析.研究结果表明,X90经慢速加热长时间保温与快速加热短时间保温所获得显微组织大不相同,当冷却速度较小(0.5-10℃/s)时,组织以多边形铁素体+珠光体为主;当冷却速度
The unplanned release of hydrocarbons from a pipeline can lead to significant pollution and/or the horrific potential of explosion and a very large fire,depending on the transported product.For this r
Gas and oil developments in cold areas and deep seas are steadily progressing.Accordingly,the construction of pipelines has expanded to the environmentally severe regions such as cold region,seismic r
腐蚀缺陷作为管道运行期间最主要的缺陷类型之一，一直是管道完整性管理的主要内容，为了保证此类缺陷下的管道完整性，管道行业先后开发了ASME B31G,ASME B31G Modified,RSTRENG,LPC,PCORRC和C-fer等六种腐蚀缺陷评估模型。本次评估推荐采用ASME B31G Modified模型，对内检测出来的缺陷深度在10％-19%的腐蚀缺陷进行了评估，最大安全操作压力与MAO
湿气管道内腐蚀评价标准(WG-ICDA)是一种独立的内腐蚀评价办法.WG-ICDA可应用于产生或者冷凝水为主要产物的陆地和离岸天然气管道,同样也能应用于湿性天然气集气管线和天然气生产管线.WG-ICDA针对的目标主要是含有湿性天然气；不属于干气内腐评价标准范围；满足此标准的可行性要求.WG-ICDA的主要目的是增强管道的内腐蚀评价；提升管道的完整性.WG-ICDA共分四个过程:预评价过程，间接检测
埋地弯头是长输油气管道中常见的结构形式.基于非线性有限元法建立了埋地弯头应力计算的数值模型.模型采用非线性土弹簧模拟土壤对管道的约束作用,采用壳单元模拟管道,以管道内压与温度为载荷,对比计算了不同管径、壁厚、弯头曲率半径与夹角、土弹簧抗力多种特性参数对管道应力的影响,分析了管道最大应力的变化规律性.计算结果表明,该方法能够较好地模拟弯头的受力过程,可为埋地弯头的设计与安全评价提供一定的参考依据.
本文研究了不同的热处理温度对超级13Cr马氏体不锈钢电化学腐蚀行为的影响.通过改变回火温度获得逆变奥氏体,借助金相组织分析、X射线衍射分析、电化学阻抗谱及动电位极化等手段,研究了逆变奥氏体对于超级13Cr腐蚀行为的影响.研究结果表明,在500℃～700℃的回火温度范围内,随着回火温度的升高,组织中碳化物析出相增多;650℃回火试样明显观察到奥氏体相的存在.极化曲线结果表明,随着回火温度的升高,腐蚀
The specimens of girth weld joint of 0813mmxl4.7mm pipeline cracked at "near-seam zone77 in tensile test.It was considered unacceptable for strain-based design pipelines in some current standards.The
In the past,the pipeline industry relied on years of research and experiences to develop a management system to ensure pipeline integrity.The pipeline integrity fulfils the design requirements through