【摘 要】
：
The catalytic performance of NO removal was studied over Mn-Ce/TiO2 catalysts prepared by different preparation parameters, such as preparation method, manganese precursor, Mn/(Mn+Ce) molar ratio and
【机 构】
：
State Key Laboratory of Green Building Materials, China Building Materials Academy, No.1 Guanzhuang
【出 处】
：
The 14th International Congress on the Chemistry of Cement (
论文部分内容阅读
The catalytic performance of NO removal was studied over Mn-Ce/TiO2 catalysts prepared by different preparation parameters, such as preparation method, manganese precursor, Mn/(Mn+Ce) molar ratio and calcination conditions.It was found that samples prepared by impregnation method, which had the largest surface area and highly dispersed active component particles, showed the best denitration activity.As manganese precursor, manganese nitrate and manganese acetate were more conducive to high denitration efficiency than manganese chloride.The highest NO conversion of 92% is achieved at the Ce/(Mn+Ce) molar ratio of 0.15, which is much higher than that of the pure manganese constituent.The increase of calcining temperature favored the crystallization of active components, leading to the decline of catalytic activity.
其他文献
If the temperature of materials to feed into rotary kiln is increased from 900℃ to 1000~1200℃, both the solid-phase reaction and liquid-phase reaction took palace in the kiln will be significant incre
The capture capacity and its mechanism of C-S-H gel to heavy metal ions (Cr, Pb, Zn, Cd, Cu) with different valence and existence form were analyzed by X-ray diffraction analysis, x-ray photoelectron
A simple co-processing model is proposed to handle domestic waste by using NSP(New Suspension Preheater)kiln, and it aims to tackle the difficulties of handling domestic waste located in ruaal areas b
Calcium sulpho-aluminate modified portland cement (SMP), containing3.0%, 5.5%, 7.0%, 9.0% of MgO were prepared.DTA, XRD, SEM and EDAX are used to investigate the effect of MgO on sintering of SMP.The
While minor impurities in the form of (A1, Fe, Mg) are understood to have substantial influences on the structure and reactivity of the siliceous cementing phases, specific details at the atomistic le
Calcium carbide Slag is one kind of industrial wastes from CaC2 hydrolysis reaction.The calcium carbide slag not only occupies the land, but also pollutes the surrounding environ.ent due to the long-t
The influence of silicon rate to the aiite-yeelimite cement clinker was investigated in this paper.The resulting clinker was analyzed for the content of free lime, sulfur and microscopical description
The effect of Fe2O3 content on properties of calcium aluminate cement is studied in this paper.The results show that setting time, compressive strength and CA+CA2 mineral content of calcium aluminate
The strip-like Mn-Ce/clay and Mn-Ce/TiO2 catalysts, which using MnOx and CeOx as active components, clay and TiO2 as supports respectively, were prepared by impregnation method.The as-prepared catalys
Grey relational analysis of grey system theory was applied to study the relationships between the heat consumption of clinker and production process parameters which base on the actual data of 2500 t