【摘 要】
：
The phase separation of glasses of the 17(CaO+MgO)-6Na2O-6AhO3-65SiO2-x(B2O3 +P2O5)(0 ≤ x ≤6) (wt%) series were investigated using DSC, XRD and SEM.The X-ray diffraction (XRD) and differential scannin
【机 构】
：
Shahe Research Institute of Glass Technology, Hebei, Xingtai 054100, China
【出 处】
：
The 24th International Conference on Glass( ICG Congress 201
论文部分内容阅读
The phase separation of glasses of the 17(CaO+MgO)-6Na2O-6AhO3-65SiO2-x(B2O3 +P2O5)(0 ≤ x ≤6) (wt%) series were investigated using DSC, XRD and SEM.The X-ray diffraction (XRD) and differential scanning calorimetry (DSC) showed that there were two amorphous phases in the glasses.
其他文献
以SiCw和SiCnm两者为增强相,采用热压工艺制备晶须与纳米颗粒混杂增强增韧的ZRC基超高温复合材料,同时对所制备的材料进行组织分析与性能测试.结果表明,SiCw主要是通过裂纹偏转、晶须桥接与晶须拔出等增韧机制；加入SiCnm,在烧结过程中提高复合材料制备时的致密度,通过细晶强化,增加裂纹的扩展,颗粒对裂纹的钉扎以及复合材料内各组分间热膨胀、弹性模量失配途径来提高材料的强韧性.其中75ZrC+1
曲梁结构广泛应用于航空航天、机械、土木等工程实际中，其固有频率和振型的精确预测对于结构设计十分重要。然而，曲率的影响导致了曲线梁结构的运动相互耦合，振动形式复杂，这给动力分析带来了不便。本文基于Timoshenko梁理论，考虑轴向拉伸、横向剪切及旋转惯性作用，采用以NURBS(非均匀有理B样条)为基函数的等几何方法，实现了精确几何的平面曲梁自由振动分析。
轴向运动连续体系统中，其动力学特性呈现为横向振动和不稳定性，横向振动使系统产生不稳定性，限制了它们的应用效果。轴向运动系统的控制方程中含有时间和空间混合偏导数项，是典型的陀螺连续体，运动微分方程中包含着丰富的动力学内容。由于技术流程的要求，在高速运动印刷包装系统中，出现张力的不均匀性是显而易见的，因此必须考虑在非均匀张力作用下，系统会产生的动力学行为。图1 所示，在非均匀张力作用下以恒定速度轴向运
To analyze the fracture problem of the nonhomogeneity high temperature superconductor(HTS)strip under electromagnetic force,we derive the real fundamental solutions based on eigenvalue and eigenvector
Inorganic color converters such as phosphor ceramic (PC) and phosphor-in-glass (PiG) have been now commercialized to replace organic resin which suffered from weak thermal and chemical stabilities for
Er3+ doped transparent oxy-fluoride glass ceramics containing LuOF nanocrystals was prepared by traditional melt-quenching and subsequent thermal treatment method.The influence of thermal treatment te
In order to get Nano-sized cordierite glass-ceramics, different kind of nucleation catalysts was tested in the cordierite base glass , such as TiO2, Zr2O3, and admixed TiO2-Zr2O3.
80V2O5-20P2O5-xSb2O3 (VPS) (x =1, 3, 5 mol%) Glasses were prepared.The crystallization stability analysis of VPS glass were investigated.The effect of Sb2O3 on crystallization lower limit temperature
Nuclear waste glasses are produced by a succession of physical and chemical interactions between a solid waste (calcine) and a glassy precursor (glass frit) through a high-temperature vitrification st
Adding Fe2O3 to sodium borosilicate (SBS) glass-forming system gives such glasses a number of valuable properties, which makes it possible to use them for producing semiconducting fibers, glass enamel